ABS 5000M TAIDA TAIWAN

121

Form：Granules | Grade：Extrusion grade

Properties:

High rigidityHigh glossImpact resistanceHigh gloss hardImpact resistanceHigh rigidityHighlightModerate impact resistanc

Typical Applications:

Household goodsVideo tape

Supplier(1)

Product Description

Certificates(4)

Datasheet

Product Description

Typical Applications:	Household goods \| Video tape
Properties:	High rigidity \| High gloss \| Impact resistance \| High gloss \| hard \| Impact resistance \| High rigidity \| Highlight \| Moderate impact resistanc

Certificates

RoHS

TDS

TDS_ISO

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 23℃	ASTM D790	77.5	Mpa
Impact strength of cantilever beam gap	23℃, 3.18 mm	ASTM D256	200	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃, 6.35 mm	ASTM D256	180	J/m
Rockwell hardness	R-Scale, 23℃	ASTM D785	115
tensile strength	Yield, 23℃, 3.18 mm	ASTM D638	44.1	Mpa
tensile strength	tensile strength	Break, 23℃, 3.18 mm	ASTM D638	37.3	Mpa
elongation	Break, 23℃, 3.18 mm	ASTM D638	30	%
Elongation at Break	23°C	ASTM D638	30	%
bending strength	23°C	ASTM D790	76	Mpa
Bending modulus	23°C	ASTM D790	2550	Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	220	J/m
tensile strength	23°C	ASTM D638	44	Mpa
Bending modulus	23℃	ASTM D790	27000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Annealed, 12.7 mm	ASTM D648	85	°C
Vicat softening temperature		ASTM D1525	103	°C
High arc combustion index	1.57 mm	UL 746	PLC 0
Hot wire ignition	1.57 mm	UL 746	PLC 3	sec
UL flame retardant rating	1.59 mm	UL 94	HB
Hot deformation temperature	1.80MPaUnannealed	ASTM D648	85	°C
Vicat softening temperature		ASTM1525	103	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃/5.0 kg	ASTM D1238	1.8	g/10 min
melt mass-flow rate	melt mass-flow rate	220℃/10.0 kg	ASTM D1238	20	g/10 min
Shrinkage rate	MD	ASTM D955	< 0.40	%
Water absorption rate	Saturation	ASTM D570	< 0.30	%
Shrinkage rate	MD	ASTM D995	<0.40	%
Water absorption rate	(23°C,24hr)	ASTM D570	<0.30	%
melt mass-flow rate	200℃/5.0Kg	ASTM D1238	1.8	g/10min
melt mass-flow rate	melt mass-flow rate	220℃/10.0Kg	ASTM D1238	20	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1E+22	Ω.cm
Dielectric strength		ASTM D149	22	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	115	R
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL -94	HB	1.50mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.