| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | JISK7112 | 1.53 g/cm³ |
| Apparent density | | JISK6720-2 | 0.50to0.60 g/cm³ |
| K-Value | | JISK6720-2 | 55.0 |
| Chlorine content | | ISO 1158 | 64.0 wt% |
| density | | JISK7112 | 1.53 g/cm³ |
| Apparent density | | JISK6720-2 | 0.50to0.60 g/cm³ |
| K-Value | | JISK6720-2 | 55.0 |
| Chlorine content | | ISO 1158 | 64.0 wt% |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| temperature | | JISK6745 | 86 °C |
| temperature | | JISK6745 | 86 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | JISK7171 | 86.0 MPa |
| tensile strength | Yield | JISK7113 | 58.0 MPa |
| Tensile strain | Break | JISK7113 | 70 % |
| Flexural modulus | | JISK7171 | 2750 MPa |
| bending strength | | JISK7171 | 86.0 MPa |
| tensile strength | Yield | JISK7113 | 58.0 MPa |
| Tensile strain | Break | JISK7113 | 70 % |
| Flexural modulus | | JISK7171 | 2750 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | JISK7111 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | JISK7111 | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 47to63 kV/mm |
| dielectric constant | | | 3.08 |
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 47to63 kV/mm |
| dielectric constant | | | 3.08 |
| dielectric constant | | | 3.20to3.60 |
| dielectric constant | | | 3.20to3.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | JISK7206 | 103 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.0E-5到7.5E-5 cm/cm/°C |
| Heat loss | | JISK6720-2 | <0.3 wt% |
| vicat | | JISK7206 | 103 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.0E-5到7.5E-5 cm/cm/°C |
| Heat loss | | JISK6720-2 | <0.3 wt% |
| Heat distortion temperature | | JISK7207 | 95.0 °C |
| Heat distortion temperature | | JISK7191-1 | 85.0 °C |
| Heat distortion temperature | | JISK7191-1 | 85.0 °C |
| Heat distortion temperature | | JISK7207 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.