ASA W90 XG

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.14 g/cm³
Melt volume flow rate		ISO1133	34.0 cm³/10min
Shrinkage rate		ISO2577	0.50to0.70 %
Shrinkage rate	Shrinkage rate		ISO2577	0.50to0.70 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO180/A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/A	14 kJ/m²
Multi axis Instrumented Impact Energy		ISO6603-2	20.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy		ISO6603-2	45.0 J
Multi axis Instrumented Peak Impact Force		ISO6603-2	4250 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force		ISO6603-2	4800 N

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2/1	2830 MPa
Tensile stress		ISO527-2/50	65.0 MPa
Tensile stress	Tensile stress		ISO527-2/50	50.0 MPa
Tensile strain		ISO527-2/50	4.0 %
Tensile strain	Tensile strain		ISO527-2/50	50 %
Flexural modulus		ISO178	2840 MPa
bending strength		ISO178	85.0 MPa
Bending Strain		ISO178	5.0 %

Thermal performance	Test Condition	Test Method	Test Result
		ISO75-2/B	112 °C
			ISO75-2/A	93.0 °C
vicat		ISO306/B50	113 °C
vicat	vicat		ISO306/B120	115 °C
		ISO11359-2	7E-05 cm/cm/°C
			ISO11359-2	7E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.