'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC OQ3820 SABIC INNOVATIVE US
36
Form：Granules | Grade：Optical grade
Properties:
Thermal stabilityHigh temperature resistan
Typical Applications:
Automotive componentsglasseslenslens
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive components | glasses | lens | lens |
| Properties: | Thermal stability | High temperature resistan |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 85.0 | J |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 | |
| -30°C | ISO 180/1U | 无断裂 | ||
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75 | kJ/m² |
| -30°C | ISO 179/1eA | 15 | kJ/m² | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | --5 | ISO 178 | 2200 | Mpa |
| 50.0mmSpan4 | ASTM D790 | 2410 | Mpa | |
| elongation | Break | ISO 527-2/50 | 140 | % |
| tensile strength | Break | ISO 527-2/50 | 71.0 | Mpa |
| Break3 | ASTM D638 | 72.0 | Mpa | |
| Yield | ISO 527-2/50 | 61.0 | Mpa | |
| Yield3 | ASTM D638 | 62.0 | Mpa | |
| bending strength | Yield,50.0mmSpan4 | ASTM D790 | 93.0 | Mpa |
| --5,6 | ISO 178 | 94.0 | Mpa | |
| elongation | Break3 | ASTM D638 | 130 | % |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Yield3 | ASTM D638 | 6.3 | % | |
| Tensile modulus | --2 | ASTM D638 | 2280 | Mpa |
| -- | ISO 527-2/1 | 2400 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 129 | °C |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 139 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 7.7E-05 | cm/cm/°C |
| TD:-40to40°C | ISO 11359-2 | 7.9E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 7.7E-05 | cm/cm/°C | |
| MD:-40to40°C | ISO 11359-2 | 7.6E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,100mmSpan9 | ISO 75-2/Ae | 126 | °C |
| Vicat softening temperature | -- | ASTM D152510 | 150 | °C |
| -- | ISO 306/B50 | 143 | °C | |
| -- | ISO 306/B120 | 144 | °C | |
| Ball Pressure Test | 75°C | IEC 60695-10-2 | 通过 | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.4 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 6.40 | cm3/10min |
| Shrinkage rate | MD:3.20mm | Internal Method | 0.60-0.80 | % |
| TD:3.20mm | Internal Method | 0.50-0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.32 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.