PA66 CM3001G15 TORAY SYN THAILAND

Form：Granules | Grade：Enhance wear resistance level

Properties:

Flame retardant

Typical Applications:

Electrical componentsElectrical appliancesAutomotive sectorElectronic field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical components \| Electrical appliances \| Automotive sector \| Electronic field
Properties:	Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C	ISO 179	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	65	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-40°C	ISO 179	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.79 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Friction coefficient - vs. Metal		Suzuki Method	0.15
Taber abraser	1000 Cycles	ISO 9352	0.400	mg
shear strength	23°C	ASTM D732	95.0	Mpa
Compressive stress	80°C	ISO 604	110	Mpa
	Compressive stress	23°C	ISO 604	180	Mpa
	Compressive stress	Compressive stress	-40°C	ISO 604	250	Mpa
bending strength	80°C	ISO 178	190	Mpa
	bending strength	23°C	ISO 178	290	Mpa
	bending strength	bending strength	-40°C	ISO 178	325	Mpa
Bending modulus	80°C	ISO 178	5800	Mpa
	Bending modulus	23°C	ISO 178	9500	Mpa
	Bending modulus	Bending modulus	-40°C	ISO 178	11600	Mpa
Tensile strain	Break, 80°C	ISO 527-2	5.0	%
	Tensile strain	Break, 23°C	ISO 527-2	2.5	%
	Tensile strain	Tensile strain	Break, -40°C	ISO 527-2	2.0	%
tensile strength	80°C	ISO 527-2	120	Mpa
	tensile strength	23°C	ISO 527-2	190	Mpa
	tensile strength	tensile strength	-40°C	ISO 527-2	235	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262	°C
Melting temperature		DSC	265	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5	cm/cm/°C
specific heat			1800	J/kg/°C
thermal conductivity			0.40	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23°C	ISO 1183	1.37	g/cm³
Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.60 - 0.90	%
Shrinkage rate	Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.50	%
Water absorption rate	24 hr, 23°C	ISO 62	0.60	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	5.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1.0E+13	ohms·cm
Dielectric strength		IEC 60243-1	20	KV/mm
Dielectric constant	23°C, 50 Hz	IEC 60250	4.60
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.40
	Dielectric constant	Dielectric constant	23°C, 1 MHz	IEC 60250	3.90
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
Arc resistance		UL 746	114	sec
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121
	Rockwell hardness	R -Sale, 80°C	ISO 2039-2	24
	Rockwell hardness	Rockwell hardness	M -Sale, 23°C	ISO 2039-2	97

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.