Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.3 % |
| Shrinkage rate | | ISO 294-4 | 1.5 % |
| Water absorption rate | | ISO 62 | 0.70 % |
| Water absorption rate | | ISO 62 | 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | ISO 7619-1 | 65 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | -- Mpa |
| Tensile stress | | ISO 527-2 | -- Mpa |
| Tensile stress | | ISO 527-2 | 55.0 Mpa |
| Tensile strain | | ISO 527-2 | -- % |
| Tensile strain | | ISO 527-2 | > 300 % |
| Nominal tensile fracture strain | | ISO 527-2 | -- % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 到 80 °C |
| drying time | | | 5.0 到 7.0 hr |
| Melt Temperature | | | 230 到 290 °C |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 70 到 80 °C |
| drying time | | | 5.0 到 7.0 hr |
| Processing (melt) temperature | | | 230 到 290 °C |
| Temperature | | | 25 到 60 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B50 | 175 °C |
| Melting temperature 2 | | ISO 11357-3 | 186 °C |
| Melting temperature 2 | | CSA LISTED | 93 到 97 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.