other	Test Condition	Test Method	Test Result	Test Unit
remarks			通用
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.3	%
melt mass-flow rate	200℃,10kg	ASTM D-1238(ISO 1133)	35	g/10min
melt mass-flow rate	melt mass-flow rate	200℃,5kg	ASTM D-1238(ISO 1133)	5.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790/ISO 178	670	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	24000	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	110
tensile strength		ASTM D638/ISO 527	480	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	15	%
Rockwell hardness		ASTM D-785	110	R scale
Impact strength of cantilever beam gap	6.4mm	ASTM D-256	22	kg.cm/cm
Bending modulus	23℃	ASTM D-790	24000	kg/cm
bending strength	23℃	ASTM D-790	670	kg/cm
elongation	Break	ASTM D-638	15	%
tensile strength	23℃	ASTM D-638	480	kg/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
UL flame retardant rating		UL -94	HB	CLASS
Hot deformation temperature	6.4mm,18.6kg/cm	ASTM D-648	85	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.04
Shrinkage rate		ASTM D-75	0.4-0.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.