Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 12到18 g/10min |
| Shrinkage rate | | | 0.40到0.60 % |
| Water absorption rate | | ASTMD570 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 109 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gardner glossiness | | ASTMD523 | 50 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-1 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ResidualStyrene3 | | 内部方法 | 0.050 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 45.0 Mpa |
| elongation | | ASTMD638 | 20 % |
| Flexural modulus | | ASTMD790 | 2350 Mpa |
| bending strength | | ASTMD790 | 69.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | DIN53453 | 10 kJ/m² |
| | ISO180 | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD15252 | 100 °C |
| | ASTMD696 | 9E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.17 W/m/K |
| Heat distortion temperature | | ASTMD648 | 102 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.