Cellulose, Regenerated 500MS
0
- Usages:Filmpackagingtape
CompareTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 90 | |
| Haze ratio | ASTM D1003 | 4.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.20 |
| Itself - Static | ASTM D1894 | 0.25 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Initial sealing temperature | 内部方法 | 90.0to160 °C | |
| oxygen permeability | ASTMF1927 | 3.00 cm³/m²/24hr | |
| Water Vapor Transmission Rate | ASTME96 | 20 g/m²/24hr | |
| film thickness | 内部方法 | 34.7 µm | |
| usage | 内部方法 | 20.0 m²/kg | |
| Secant modulus | ASTM D882 | >3000 MPa | |
| ASTM D882 | >1500 MPa | ||
| tensile strength | ASTM D882 | 125 MPa | |
| ASTM D882 | 70.0 MPa | ||
| elongation | ASTM D882 | 22 % | |
| ASTM D882 | 70 % | ||
| Sealing emphasis | 内部方法 | 1.8 N/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.