PC GS2010MPH MITSUBISHI ENGINEERING JAPAN

Form：Granules | Grade：Injection grade

Properties:

enhanceFiller: Glass fiber reinf10%Filler by weight

Typical Applications:

Fiber grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fiber grade
Properties:	enhance \| Filler: Glass fiber reinf \| 10% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	55	kJ/m²
machinability	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			80-120	°C
Screw speed			50-100	rpm
Processing temperature			280-300	°C
	Processing temperature			290-310	°C
	Processing temperature	Processing temperature			270-290	°C
Dry conditions			热风干燥 120℃---約4-8小时
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	135	Mpa
Bending modulus		ISO 178	4000	Mpa
Tensile strain	Break	ISO 527-2	2.9	%
tensile strength	Break	ISO 527-2	78.0	Mpa
Tensile modulus		ISO 527-2	4500	Mpa
Elongation at Break		ASTM D638/ISO 527	10	%
bending strength		ASTM D790/ISO 178	90	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2700	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	2900	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D696/ISO 11359	5.8.E-05	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.14	%
Shrinkage rate	MD:3.20mm		0.30-0.50	%
Shrinkage rate	Shrinkage rate	TD:3.20mm		0.40-0.60	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	10	g/10min
Shrinkage rate		ASTM D955	0.3 - 0.5	%
density		ASTM D792/ISO 1183	1.26
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC GS2010MPH MITSUBISHI ENGINEERING JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index