'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPA AT-6115HS BK324 SOLVAY USA
150
Form：Granules
Properties:
High temperature resistanThermal stabilityFiller: Glass fiber reinf15%Filler by weight
Typical Applications:
Industrial applicationsAutomotive ApplicationsValves/valve componentsParts under the hood of a carVehicle electronicsApplication in the automotive fieldMachine/mechanical componentsLaptop casecurrencyMetal substitutionIndustrial componentsShell
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Industrial applications | Automotive Applications | Valves/valve components | Parts under the hood of a car | Vehicle electronics | Application in the automotive field | Machine/mechanical components | Laptop case | currency | Metal substitution | Industrial components | Shell |
| Properties: | High temperature resistan | Thermal stability | Filler: Glass fiber reinf | 15% | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 76 | kJ/m² |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | 100°C | ISO 178 | 2340 | Mpa |
| 23°C | ISO 178 | 4270 | Mpa | |
| ASTM D790 | 4410 | Mpa | ||
| Tensile strain | Break,24°C | ISO 527-2 | 7.7 | % |
| Break,23°C | ISO 527-2 | 4.1 | % | |
| elongation | Break | ASTM D638 | 3.4 | % |
| tensile strength | Break,24°C | ISO 527-2 | 68.3 | Mpa |
| shear strength | ASTM D732 | 56.5 | Mpa | |
| compressive strength | ASTM D695 | 100 | Mpa | |
| bending strength | 100°C | ISO 178 | 66.9 | Mpa |
| 23°C | ISO 178 | 170 | Mpa | |
| ASTM D790 | 165 | Mpa | ||
| Tensile modulus | ASTM D638 | 5380 | Mpa | |
| 23°C | ISO 527-2 | 5200 | Mpa | |
| 100°C | ISO 527-2 | 3100 | Mpa | |
| tensile strength | ASTM D638 | 122 | Mpa | |
| Break,23°C | ISO 527-2 | 126 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD：100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| TD：0to100°C | ASTME831 | 9E-05 | cm/cm/°C | |
| MD：100to200°C | ASTME831 | 3E-05 | cm/cm/°C | |
| MD：0to100°C | ASTME831 | 2.2E-05 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 305 | °C | |
| ASTM D3418 | 305 | °C | ||
| Hot deformation temperature | 1.8MPa,Annealed | ASTM D648 | 260 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 251 | °C | |
| 0.45MPa,Unannealed | ISO 75-2/B | 298 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | TD | ASTM D955 | 1.1 | % |
| MD | ASTM D955 | 1.0 | % | |
| Water absorption rate | 24hr | ASTM D570 | 0.20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.