Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | Equilibrium | ASTM D570 | 0.040 % |
| density | | | 1.30 g/cm³ |
| Shrinkage rate | | | 1.0 % |
| Shrinkage rate | | | 1.3 % |
| MeltViscosity | | ASTM D3835 | 300to350 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 100 |
| Shore hardness | | ASTM D2240 | 86 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 4200 MPa |
| tensile strength | | ASTM D638 | 110 MPa |
| elongation | | ASTM D638 | 20to25 % |
| Flexural modulus | | ASTM D790 | 4100 MPa |
| bending strength | | ASTM D790 | 185 MPa |
| compressive strength | | ASTM D695 | 135 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D3418 | 372 °C |
| Heat distortion temperature | | ASTM D648 | 175 °C |
| Continuous use temperature | | UL 746B | 280 °C |
| Glass Transition Temperature | | ASTM D3418 | 152 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.