Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | % | 0.12到0.50 |
| Shrinkage rate | | mm/mm | 50.8E-3到154.9E-3 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 103到115 |
| | | 55到95 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | % | 86.9到92.1 |
| Haze ratio | | % | 0.20到2.3 |
| gloss | | | 107到162 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 42.28到58.0 |
| fracture | | Mpa | 23.38到53.17 |
| yield | | Mpa | 43.03到50.0 |
| fracture | | % | 30到340 |
| fracture | | % | 97到230 |
| yield | | % | 4.0到7.0 |
| yield | | % | 4.0到7.4 |
| yield | | Mpa | 62.0到77.93 |
| fracture | | Mpa | 27.45到58.0 |
| film | Test Condition | Test Method | Test Result |
|---|
| MD | | Mpa | 1496.55到2200.0 |
| MD | | g | 25到1400 |
| Water vapor permeability | | g/100 | 0.15到8.7 |
| Falling hammer impact | | g | 390到880 |
| MD: Fracture | | Mpa | 23.03到59.59 |
| fracture | | Mpa | 20.0到45.03 |
| TD: Fracture | | Mpa | 18.14到58.9 |
| TD: Yield | | Mpa | 38.69到52.41 |
| Tear resistance of pants | | n/m | 523.01到1823.01 |
| oxygen permeability | | cm³·mil/100 | 25到84 |
| MD: Surrender | | % | 3.0到7.3 |
| TD: Fracture | | % | 4.0到550 |
| fracture | | % | 38到710 |
| Film thickness - tested | | mil | 0.98到13 |
| TD | | Mpa | 1241.38到2124.14 |
| TD | | g | 12到1700 |
| TD: Yield | | % | 4.0到7.3 |
| MD: Surrender | | Mpa | 40.76到52.0 |
| MD: Fracture | | % | 4.0到410 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | sec | 128到158 |
| dielectric strength | | V/mil | 400到410 |
| dielectric constant | | | 2.40到3.20 |
| Dissipation Factor | | | 4.7E-3到0.020 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | W/m2k | 0.23到0.26 |
| | mm/mm/°C | 71.1E-5到203.2E-5 |
| Glass Transition Temperature | | °C | 71到110 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.