Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ISO1183 | 1.40 g/cm³ |
| Melt volume flow rate | | ISO1133 | 11.0 cm³/10min |
| Shrinkage rate | | ISO294-4 | 2.1 % |
| Shrinkage rate | | ISO294-4 | 2.1 % |
| Water absorption rate | | ISO62 | 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 145 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC60695-11-10,-20 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO9988-1 | POM-K,M-GNR,04-002 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2700 MPa |
| Tensile stress | Yield | ISO527-2/50 | 65.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 9.0 % |
| Nominal tensile fracture strain | | ISO527-2/50 | 28 % |
| Tensile creep modulus | | ISO899-1 | 1300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 170 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 180 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| | IEC60250 | 3.80 |
| Dissipation Factor | | IEC60250 | 5E-03 |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO75-2/A | 100 °C |
| melting temperature | | ISO11357-3 | 167 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Maximum operating temperature - sortcycle operation | | | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.