Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ISO 2039-2 | 100 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 195 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | ED3002/EF2001 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.6 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.46 g/cm³ |
| water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| volume resistivity | | IEC 60093 | 4E+16 ohms·cm |
| dielectric strength | 3.00mm | IEC 60243-1 | 26 kV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 139 MPa |
| Tensile strain | Break | ISO 527-2 | 2.0 % |
| flexural modulus | | ISO 178 | 9000 MPa |
| bending strength | | ISO 178 | 180 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.