ABS PA-757F TAIWAN CHIMEI

372

Form：Granules

Properties:

High gloss

Typical Applications:

Household goodsLighting fixturesNon specific food applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Household goods \| Lighting fixtures \| Non specific food applications
Properties:	High gloss

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			食品级、低残单
purpose			食品容器、小家电
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638/ISO 527	34	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	47	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	30	%
Bending modulus		ASTM D790/ISO 178	2.2	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	76	kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	21	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	19	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	9	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	98	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	83	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	104	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8.6×10-5	mm/mm.℃
Vickers softening temperature	1 Kg,50℃/hr	ISO 306	104	°C
Hot deformation temperature	1.8 MPa Unannealed	ISO 75/A	83	°C
linear expansion coefficient		ISO 11359	8.6 x 10-5
Flame Rating	1.5mm	UL -94	HB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.05
Shrinkage rate		ASTM D955	0.4-0.7	%
melt mass-flow rate		ASTM D1238/ISO 1133	18	g/10min
Tensile strength, 50 mm/min, yield		ISO 527	47	Mpa
Melt index	220℃×10KG	ISO 1133	18	ml/10 min
Molding shrinkage rate		ISO 294-4	0.4-0.7	%
Elongation at Break	50 mm/min, break	ISO 527	30	%
bending strength		ISO 178	76	Mpa
Bending modulus of elasticity		ISO 178	2.2	GPa
Impact strength of cantilever beam gap	23 ℃ Notched	ISO 180/1A	19
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃ Notched		KJ/m2
Charpy Notched Impact Strength	23℃ Notched	ISO 179	21	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.