Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 0.70 g/10min |
| Shrinkage rate | | ASTM D955 | 0.20-0.40 % |
| Shrinkage rate | | ASTM D955 | 1.4-1.6 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 |
| Shore hardness | | ASTM D2240 | 91 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180 | 56 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 960 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 10500 Mpa |
| Tensile modulus | | ISO 527-2/1A/1 | 11400 Mpa |
| tensile strength | | ASTM D638 | 158 Mpa |
| tensile strength | | ISO 527-2/1A/5 | 165 Mpa |
| tensile strength | | ASTM D638 | 158 Mpa |
| Nominal tensile fracture strain | | ISO 527-2/1A/5 | 2.7 % |
| Nominal tensile fracture strain | | ASTM D638 | 2.7 % |
| Flexural modulus | | ASTM D790 | 10300 Mpa |
| Flexural modulus | | ISO 178 | 10700 Mpa |
| bending strength | | ASTM D790 | 271 Mpa |
| bending strength | | ISO 178 | 246 Mpa |
| bending strength | | ASTM D790 | 261 Mpa |
| compressive strength | | ASTM D695 | 169 Mpa |
| shear strength | | ASTM D732 | 93.1 Mpa |
| Poisson's ratio | | | 7.58 0.34 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ASTM D3835 | 850 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | >1.9E+17 ohms |
| Volume resistivity | | ASTM D257 | 1.9E+17 ohms·cm |
| dielectric strength | | ASTM D149 | 17 KV/mm |
| dielectric constant | | ASTM D150 | 3.44 |
| dielectric constant | | ASTM D150 | 3.44 |
| dielectric constant | | ASTM D150 | 3.41 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 3E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 315 °C |
| Glass Transition Temperature | | ASTM D3418 | 150 °C |
| melting temperature | | ASTM D3418 | 340 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.7E-05 cm/cm/°C |
| specific heat | | DSC | 1300 J/kg/°C |
| specific heat | | DSC | 1730 J/kg/°C |
| thermal conductivity | | ASTME1530 | 0.29 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.