Ether Neostar™ FN007

Compare

Technical Data Sheet

physical property	Test Method	Test Result
density	ASTM D792	1.13 g/cm³
melt mass-flow rate	ASTM D1238	4.0 g/10min
Water absorption rate	ASTM D570	0.40 %
intrinsic viscosity	内部方法	1.2

hardness	Test Condition	Test Method	Test Result
Shore hardness		ASTM D2240	95
Shore hardness	Shore hardness		ASTM D2240	55

optical performance	Test Condition	Test Method	Test Result
gloss		ASTM D2457	73
refractive index		ASTM D542	1.510
transmissivity		ASTM D1003	91.0 %
transmissivity	transmissivity		ASTM D1003	94.0 %
Haze ratio		ASTM D1003	1.0 %

Supplementary Information	Test Condition	Test Method	Test Result
tear strength		ASTM D1004	350 N

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	170 MPa
tensile strength		ASTM D638	13.0 MPa
tensile strength	tensile strength		ASTM D638	23.0 MPa
elongation		ASTM D638	38 %
elongation	elongation		ASTM D638	400 %
Flexural modulus		ASTM D790	150 MPa
coefficient of friction		ASTM D1894	>1.0

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	40 J/m

elastomer	Test Condition	Test Method	Test Result
Kappa modulus		ASTM D1043	930 MPa
Kappa modulus	Kappa modulus		ASTM D1043	240 MPa

film	Test Condition	Test Method	Test Result
elongation		ASTM D882	20 %
	elongation		ASTM D882	330 %
	elongation	elongation		ASTM D882	>550 %
OTr		ASTM D1434	940 cm³/m²/24hr
Water Vapor Transmission Rate		ASTMF372	150 g/m²/24hr
film thickness			130 µm
Secant modulus		ASTM D882	197 MPa
Secant modulus	Secant modulus		ASTM D882	221 MPa
tensile strength		ASTM D882	11.2 MPa
	tensile strength		ASTM D882	41.5 MPa
	tensile strength	tensile strength		ASTM D882	18.1 MPa
elongation		ASTM D882	46 %

Thermal performance	Test Condition	Test Method	Test Result
Fusion temperature		ASTME793	27.0 kJ/kg
brittle temperature		ASTM D746	<-75.0 °C
Glass Transition Temperature		DSC	-3.00 °C
vicat		ASTM D15256	170 °C
melting temperature		ASTM D3418	205 °C
Crystallization peak temperature		DSC	140 °C
Linear coefficient of thermal expansion		ASTM D696	1.5E-04 cm/cm/°C
specific heat		DSC	1600 J/kg/°C
	specific heat		DSC	1800 J/kg/°C
		specific heat		DSC	2000 J/kg/°C
			specific heat		DSC	2300 J/kg/°C
				specific heat		DSC	3100 J/kg/°C
				specific heat	specific heat		DSC	2300 J/kg/°C
thermal conductivity		ASTMC177	0.19 W/m/K

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.