Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| Shrinkage rate | | ISO 294-4 | 1.6to1.8 % |
| Shrinkage rate | | ISO 294-4 | 1.8to2.0 % |
| density | | ISO 1183 | 1.28 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2100 MPa |
| tensile strength | | ISO 527-2 | 50.0 MPa |
| Tensile strain | | ISO 527-2 | 50 % |
| Flexural modulus | | ISO 178 | 2100 MPa |
| bending strength | | ISO 178 | 75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 19 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 155 °C |
| Heat distortion temperature | | ISO 75-2/A | 55.0 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.