Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 15 g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.60 % |
| Water absorption rate | | ASTM D570 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 92 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.490 |
| transmissivity | | ASTM D1003 | 92.0 % |
| Haze ratio | | ASTM D1003 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 69.0 Mpa |
| elongation | | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 3040 Mpa |
| bending strength | | ASTM D790 | 98.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 11 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 91.0 °C |
| Thermal deformation temperature under load | | ASTM D648 | 87.0 °C |
| vicat | | ASTM D15253 | 100 °C |
| vicat | | ASTM D15254 | 92.0 °C |
| | ASTM D696 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.