Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.55 g/cm³ |
| Water absorption rate | | ISO 62 | 0.13 % |
| Shrinkage rate | | ISO 294-4 | 0.4-0.8 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4-0.8 % |
| Water absorption rate | | ASTM D-570 | 0.09 % |
| density | | ASTM D-792 | 1.55 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy impact strength | | ISO 179 | 40 kJ/m² |
| Charpy impact strength | | ISO 179 | 10 kJ/m² |
| Flexural modulus | | ASTM D-790 | 8000 Mpa |
| tensile strength | | ASTM D-638 | 120 Mpa |
| elongation | | ASTM D-638 | 4.2 % |
| bending strength | | ASTM D-790 | 190 Mpa |
| Impact strength of cantilever beam gap | | ASTM D-256 | 80 J/m |
| Rockwell hardness | | ASTM D-785 | 88 M Scale |
| tensile strength | | ISO 527 | 135 Mpa |
| elongation | | ISO 527 | 2.5 % |
| bending strength | | ISO 178 | 220 Mpa |
| Flexural modulus | | ISO 178 | 10500 Mpa |
| Notch impact strength | | ISO 179(1eA) | 10 kJ/m² |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume Resistivity | | ASTM D-257 | 1014 Ω.cm |
| Loss factor | | ASTM D-150 | 2.5×10-2 106Hz |
| dielectric strength | | ASTM D-149 | 21 MV/m |
| dielectric constant | | ASTM D-150 | 3.0 106Hz |
| dielectric constant | | IEC 60250 | 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Coefficient of thermal expansion | | ASTM D-696 | 2.5 10-5℃mm/mm/℃ |
| Heat Deflection Temperature | | ASTM D-648 | 208 °C |
| Heat Deflection Temperature | | ISO 75f | 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.