ABS CL
70
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | DENKA Method | 0.4 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Total Light Transmittance | ISO 13468-1(JIS K7361) | 91 % | |
| Haze ratio | ISO 14782(JIS 7136) | 2.0 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133(JIS K7210) | 2.7 g/10min | |
| ISO 1133(JIS K7210) | 34 g/10min | ||
| density | ISO 1183(JIS K7112) | 1080 kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO 527-1 | 42 Mpa | |
| Flexural modulus | ISO 178(JIS K7171) | 2000 Mpa | |
| bending strength | ISO 178(JIS K7171) | 62 Mpa | |
| Charpy Notched Impact Strength | ISO 179(JIS K7111) | 14 KJ/m | |
| Rockwell hardness | ISO 2039-2(JIS K7202) | 31 M |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-1 | 64 °C | |
| vicat | ISO 306(JIS K7206) | 80 °C | |
| combustibility | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.