Epoxy Ad-Tech Epoxy EL-301
0
- Usages:Moldsmoldstoolsadhesiveslaminates
CompareTechnical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermosetting components | 25to30 min | ||
| Thermosetting mixed viscosity | ASTM D2393 | 2000 cP | |
| stripping time | 4300to7200 min | ||
| Thermosetting components | Resin | 按重量计算的混合比:100按容量计算的混合比:3.5 | |
| Hardener | 按重量计算的混合比:25按容量计算的混合比:1.0 |
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | ASTM D1895 | 1.12 g/cm³ | |
| Shrinkage rate | ASTM D955 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ASTM D2240 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 9860 MPa | |
| bending strength | Yield | ASTM D790 | 228 MPa |
| compressive strength | ASTM D695 | 92.3 MPa | |
| Tensile modulus | ASTM D638 | 16100 MPa | |
| tensile strength | Yield | ASTM D638 | 154 MPa |
| Break | ASTM D638 | 243 MPa | |
| elongation | Yield | ASTM D638 | 6.2 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 80.0 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 4.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.