PA6 BKV50 LANXESS GERMANY

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	85	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	85	kJ/m²
tensile strength	23°C	ISO 527-2	215	Mpa
Elongation at Break	23°C	ISO 527-2	2.70	%
Tensile modulus	23°C	ISO 527-2	16200	Mpa
bending strength	23°C	ISO 178	340	Mpa
Bending modulus	23°C	ISO 178	15000	Mpa
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	95	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	17	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	220	°C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	210	°C
Vicat softening temperature	Melting Temperature	ISO 11357-3	222	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD2.0mm	ISO 294-4	0.19	%
Shrinkage rate	Shrinkage rate	TD2.0mm	ISO 294-4	0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	7E+14	Ω.cm
Dielectric strength	1.00mm	IEC 60243-1	35	KV/mm
Dielectric constant	23°C	IEC 60250	4.70	100HZ
Dielectric constant	Dielectric constant	23°C	IEC 60250	4.20	1MHz
Dissipation factor	23°C	IEC 60250	0.014	100HZ
	Dissipation factor	23°C	IEC 60250	0.017	1MHz
	Dissipation factor	Dissipation factor	相对漏电起痕指数	IEC 60112	400	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	232	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.