EAA PRIMACOR™ 5980I DOW USA
758
- Properties:High gloss
- Usages:Power tools
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238,ISO1133 | 14 g/10min | |
| ASTMD1238,ISO1133 | 300 g/10min | ||
| Content of comonomer 4 | 内部方法 | 20.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD2240,ISO868 | 50 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 300 g/10min | |
| Monomer content | % | Internal Method 20.5 | |
| melt mass-flow rate | ASTM D-1238 | 300 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus -2% secant | ASTMD638,ISO527-2 | 33.1 Mpa | |
| tensile strength | ASTMD638,ISO527-2 | 9.65 Mpa | |
| elongation | ASTMD638,ISO527-2 | 390 % | |
| Tensile modulus -2% Secant | ASTM D-638 | 33.1 MPa | |
| ISO 527-2 | 33.1 MPa | ||
| tensile breaking strength | ASTM D-638 | 9.65 MPa | |
| ISO 527-2 | 9.65 MPa | ||
| tensile elongation at break | ASTM D-638 | 390 % | |
| ISO 527-2 | 390 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTMD1525,ISO306 | 42.2 °C | |
| 内部方法 | 77.2 °C | ||
| vicat | ASTM D-1525 | 42.2 ℃ | |
| ISO 306 | 42.2 ℃ | ||
| melting temperature | ℃ | Internal Method 77.2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.