PA66 G4000HSL NC01 INVISTA USA

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityGlass fiber reinforceddimensional stability

Typical Applications:

Electrical fieldElectronic fieldAutomotive sector

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Automotive sector
Properties:	Thermal stability \| Glass fiber reinforced \| dimensional stability

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			40%玻纤增强
purpose			汽车配件
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	320	Mpa
Bending modulus		ISO 178	10300	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	225	Mpa
Tensile modulus		ISO 527-2	12300	Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	13	kJ/m²
Charpy Notched Impact Strength	23℃	ISO 179	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-40℃	ISO 179	10	kJ/m²
bending strength		ISO 178	320	Mpa
Bending modulus		ISO 178	10300	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	225	Mpa
Tensile modulus		ISO 527-2	12300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
Melting temperature		ISO 11357-3	262	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250	°C
Melting temperature		ISO 11357-3	262	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.1	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.70	%
Shrinkage rate	MD:2.00mm	ISO 294-4	0.35-0.45	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	ISO 294-4	0.85-0.95	%
Water absorption rate	Equilibrium, 23℃, 50% RH	ISO 62	1.1	%
Water absorption rate	Water absorption rate	23℃, 24 hr	ISO 62	0.70	%
Shrinkage rate	MD: 2.00 mm	ISO 294-4	0.35-0.45	%
Shrinkage rate	Shrinkage rate	TD: 2.00 mm	ISO 294-4	0.85-0.95	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.