EVA UL00218 Lianhong Group
0
- Properties:Without adding opening agents and smoothing agentswith antioxidantsthe recommended processing temperature range is 100 ℃ -190 ℃the recommended processing temperature should not exceed 240 ℃a typical foaming temperature of 175 ℃a typical blowing temperature of 170 ℃and the specific process design should be adjusted according to the equipment and product
- Usages:Suitable for foaminginjection moldingand extrusion products
Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
density | ExxonMobil 方法 | 0.941 g/cm3 | |
melt mass-flow rate | ASTM D1238 | 2.5 g/10min | |
Vinyl acetate content | ExxonMobil 方法 | 18 wt% |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Nominal fracture strain | GB/T 1040.2-2006 | 800 % | |
Shore hardness | GB/T 2411-2008 | 88 | |
Tensile stress | GB/T 1040.2-2006 | 16 MPa |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
melting temperature | ASTM D3418 | 86 ℃ | |
vicat | ASTM D31525 | 62 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.