Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | DIN16901 | 1.8到3.0 % |
| Water absorption rate | | | <0.10 % |
| density | | ISO1183 | 1.44 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1fU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1fU | 83 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2300 MPa |
| Tensile stress | Break | ISO527-2 | 48.0 MPa |
| Tensile strain | Yield | ISO527-2 | 15 % |
| Flexural modulus | | ISO178 | 2000 MPa |
| Bending stress | | ISO178 | 70.0 MPa |
| Bending Strain | | ISO178 | 20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+13 ohms |
| insulation resistance | | IEC60167 | >1.0E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | DIN52612 | 0.20 W/m/K |
| Heat distortion temperature | | ISO75-2/A | 105 °C |
| Continuous use temperature | | UL746B | 100 °C |
| Maximum operating temperature - SharrTerm | | | 120 °C |
| vicat | | ISO306/A | 155 °C |
| | DIN53752 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.