Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.07 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 9.00 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 105 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 45 mm/min |
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 30 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 30 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 160 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 220 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2/50 | 49.0 MPa |
| Tensile strain | | ISO 527-2/50 | 3.0 % |
| Tensile strain | | ISO 527-2/50 | >15 % |
| Flexural modulus | | ISO 178 | 2300 MPa |
| bending strength | | ISO 178 | 77.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 2400 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 38 kV/mm |
| relative permittivity | | IEC 60250 | 3.10 |
| relative permittivity | | IEC 60250 | 3.00 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 99.0 °C |
| vicat | | ISO 306/B50 | 105 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/B | 106 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.