Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.16 g/cm³ |
| melt mass-flow rate | | ISO1133 | 5.3 g/10min |
| Melt volume flow rate | | ISO1133 | 5.00 cm³/10min |
| MediumDensity | | | 1.02 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.40 % |
| Shrinkage rate | | ISO294-4 | 0.20 % |
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 38 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Flammability level | | IEC60695-11-10,-20 | HB |
| Limiting Oxygen Index | | ISO4589-2 | 20 % |
| FMVSS flammability | | FMVSS302 | SE |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| TensileCreepModule | | ISO899-1 | 50.0 MPa |
| Tensile creep modulus | | ISO899-1 | 40.0 MPa |
| Tensile stress | | ISO527-2 | 4.10 MPa |
| Tensile stress | | ISO527-2 | 7.30 MPa |
| Tensile modulus | | ISO527-2 | 56.0 MPa |
| Tensile stress | Break | ISO527-2 | 26.0 MPa |
| Tensile stress | | ISO527-2 | 2.40 MPa |
| Tensile strain | Break | ISO527-2 | >300 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Tensile impact strength | | ISO8256/1 | 230 kJ/m² |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| TearStrength-Flow | | ISO34-1 | 110 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 5.20 |
| | IEC60250 | 4.70 |
| Dissipation Factor | | IEC60250 | 0.011 |
| Dissipation Factor | | IEC60250 | 0.053 |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 2E+14 ohms |
| Volume resistivity | | IEC60093 | 7E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 18 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 150 °C |
| | ISO11359-2 | 2.2E-04 cm/cm/°C |
| Glass Transition Temperature | | ISO11357-2 | -50.0 °C |
| | ISO11359-2 | 2.2E-04 cm/cm/°C |
| EffectiveThermal Diffusivity | | | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.