HDPE PC4012 Malaysia ETILINAS
0
- Properties:High density copolymers have good resistance to environmental stress cracking
- Usages:Coated metal pipe
Technical Data Sheet
Basic performance | Test Condition | Test Method | Test Result |
---|---|---|---|
melt mass-flow rate | ISO 1133: Condition 18 | 1.2 g/10min | |
density | ISO 1872/1 | 953 kg/m | |
ISO 1183 | 951 kg/m | ||
Carbon black content | ISO 6964 | 2.25 % | |
melt mass-flow rate | ISO 1133: Condition 4 | 0.3 g/10min |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile stress | ISO R527:Type 2 | 23 MPa | |
elongation | Break | ISO R527:Type 2 | >600 % |
Flexural modulus | ISO 178 | 750 MPa | |
Shore hardness | ISO 868 (1sec) | 62 | |
Environmental stress cracking resistance | ASTM D-1693B | >1000 Hours |
Other performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Oxidation induction time (OIT) | ISO TR10837 | >20 min |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
dielectric strength | ASTM D-149 | >25 kV/mm | |
Volume resistivity | ASTM D-257 | >10 Ω.cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
vicat | ISO 306 A | 120 ℃ | |
thermal conductivity | W/m℃ | BS 874(at 23℃) 0.4 | |
brittle temperature | ASTM D-746 | <-100 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.