Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.50 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.30 % |
| Water absorption rate | | ASTM D570 | 0.040 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 103 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 11000 MPa |
| bending strength | | ASTM D790 | 255 MPa |
| Tensile modulus | | ASTM D638 | 12400 MPa |
| tensile strength | | ASTM D638 | 186 MPa |
| elongation | Break | ASTM D638 | 2.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 8.0 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2.5 ohms·cm |
| Surface Resistivity | | ASTM D257 | 5.1 ohms |
| dielectric strength | | ASTM D149 | 240 kV/mm |
| dielectric constant | | ASTM D150 | 3.30 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 321 °C |
| Glass Transition Temperature | | ASTME1356 | 177 °C |
| melting temperature | | DSC | 360 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare