Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.950to0.954 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 55to65 g/10min |
| melt mass-flow rate | | ISO 1133 | 2.5to3.3 g/10min |
| Environmental stress cracking resistance | | ISO 16770 | 8.00 hr |
| Melt flow ratio | | | 17.0to25.0 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 61 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/50 | >1000 % |
| Tensile modulus | | ISO 527-2/1 | 1050 MPa |
| tensile strength | Yield | ISO 527-2/50 | 25.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 30.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 10 % |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-3/50 | 26.0 MPa |
| elongation | Break | ISO 527-3/50 | 490 % |
| Dart impact | | ASTM D1709 | 30 g |
| Elmendorf tear strength | | | 458.9 g/2.5cm |
| Elmendorf tear strength | | | 4920.1 g/2.5cm |
| film thickness | | | 20to80µm |
| tensile strength | | ISO 527-3/50 | 41.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-80.0 °C |
| vicat | | ISO 306/B50 | 73.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.