Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 0.910 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 7.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 85 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTMD2457 | 51 |
| Haze ratio | | ASTMD1003 | 82 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Thermal-oxidativeDeterioration | | TPE | >15.0 day |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 1620 MPa |
| Tensile strength - transverse flow rate | Yield | ASTMD638 | 36.3 MPa |
| Tensile strength - transverse flow rate | Break | ASTMD638 | 26.5 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 20 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 20 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 29 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 102 °C |
| vicat | | ASTMD1525 | 150 °C |
| melting temperature | | ASTMD2117 | 163 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.