LCP ZENITE® 6130L-BK010
90
- Properties:LubricityenhanceGlass fiber reinforcedFiller: Glass fiber reinf30%Filler by weight
- Usages:Electrical fieldElectronic fieldAerospace ApplicationsAutomotive sectorCommunication equipmentAerospace ApplicationsCommunication equipmentApplication in the automotive field
Compare
View PricesTechnical Data Sheet
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 12000 Mpa | |
| Tensile strain | ISO 527-2/1A/5 | 1.8 % | |
| tensile strength | ISO 527-2/1A/5 | 130 Mpa | |
| Tensile modulus | ISO 527-2/1A/1 | 13000 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 内部方法 | 5E-03 | |
| IEC 60250 | 0.031 | ||
| relative permittivity | 内部方法 | 4.16 | |
| IEC 60250 | 4.00 | ||
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+16 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 7E-05 cm/cm/°C | |
| ISO 11359-2 | 3E-06 cm/cm/°C | ||
| melting temperature | ISO 11357-3 | 335 °C | |
| Heat distortion temperature | ISO 75-2/A | 265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.