Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 26 wk |
| | | 按重量计算的混合比:1.0按容量计算的混合比:1.0 |
| | | 按重量计算的混合比:1.0按容量计算的混合比:1.0 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Black |
| Color | | | Colorless |
| density | | | 1.47 g/cm³ |
| density | | | 1.47 g/cm³ |
| | ASTM D2393 | 1.2 Pa·s |
| | ASTM D2393 | 1.2 Pa·s |
| Curing Time | | | 0.25 hr |
| Curing Time | | | 1.0 hr |
| Curing Time | | | 24 hr |
| Curing Time | | | 120 min |
| | ASTM D2393 | 1.2 Pa·s |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Hardness (Shore) | Shore A | ASTM D2240 | 60 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 3.45 MPa |
| elongation | Break | ASTM D412 | 100 % |
| tear strength | | ASTM D624 | 2.63 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 3E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| dielectric constant | | ASTM D150 | 3.40 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 2.2E-04 cm/cm/°C |
| thermal conductivity | | | 0.31 W/m/K |
| Usage temperature | | | -55-204 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare