Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Fuzzy coefficient (Haze) | | ISO 14782 | 0.5 % |
| transmittance | | ASTM D1003/ISO 13468 | 92 % |
| refractive index | | ASTM D542/ISO 489 | 1.49 |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 高品质玻璃杯 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 49 kg·cm/cm(J/M)ft·lb/in |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 2.8 kg·cm/cm(J/M)ft·lb/in |
| tensile strength | | ASTM D638/ISO 527 | 52 kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 40 % |
| Rockwell hardness | | ASTM D785 | 68（M scale） |
| Flexural modulus | | ASTM D790/ISO 178 | 1.9 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 76 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | >10^16 Ω |
| dielectric constant | | ASTM D150/IEC 60250 | 3.7(60Hz) |
| arc resistance | | ASTM D495/IEC 60112 | 无痕迹 |
| Volume resistivity | | ASTM D257/IEC 60093 | >10^13 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.16 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 6（230℃/37.3N ） g/10min |
| Water absorption rate | | ASTM D570/ISO 62 | 0.3 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D1525/ISO R306 | 85 ℃（℉） |
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 6x10^-5 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.