Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.90 到 1.3 | % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.70 到 1.1 | % |
| water content | | | < 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 50 | |
| Rockwell hardness | R 计秤 | ISO 2039-2 | 95 | |
| tensile strength | 断裂 | ISO 527-2 | 46.0 | Mpa |
| elongation | 断裂 | ISO 527-2 | 40 | % |
| Bending modulus | | ISO 178 | 1800 | Mpa |
| bending strength | | ISO 178 | 76.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 50.0 | °C |
| Melting temperature | | ISO 11357-3 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTM D257 | 1.0E+12 | ohms |
| Volume resistivity | | ASTM D257 | 1.0E+13 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Dehumidification desiccant | | | 80 | °C |
| Vacuum drying machine | | | 100 | °C |
| drying time | | | 2.0 到 4.0 | hr |
| Temperature at the rear of the barrel | | | 175 到 185 | °C |
| Temperature in the middle of the barrel | | | 210 到 215 | °C |
| Temperature at the front of the material cylinder | | | 215 到 220 | °C |
| Spray nozzle temperature | | | 220 到 225 | °C |
| Mold temperature | | | 50 到 70 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.