HIPS 622XP
0
- Properties:Excellent printabilityhigh impact resistanceand good surface finish
- Usages:sheet
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.04 g/cm3 | |
| Dissolved volume flow rate | ISO 1133 | 4.30 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| Water absorption rate | ISO 62 | <0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO 527-2/50 | 22.0 MPa |
| Break | 20.0 | ||
| Tensile strain | Yield | ISO 527-2/50 | 1.8 % |
| Fracture rate | ISO 527-2/50 | 70 % | |
| bending strength | ISO 178 | 32.0 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 9.5 kJ/m2 | |
| Ball Indentation Hardness | ISO 2039-1 | 80.0 MPa | |
| Tensile modulus | ISO 527-2 | 1800 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | 82.0 ℃ | |
| vicat | ISO 306/B50 | 89.0 ℃ | |
| Linear expansion coefficient | DIN 53752 | 0.000080 cm/cm./℃ | |
| thermal conductivity | DIN 42612 | 0.16 W/m/k |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.