HIPS POLYREX® PH-879 TAIWAN CHIMEI
737
- Properties:High mobilityFlame retardant
- Usages:Wire and cable
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | ASTM D1238/ISO 1133 | 10.0 | g/10min | |
| ASTM D-1238 | 10.0 | (Cond.G)g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 7.0(1.28) | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 8.5(1.56) | kg·cm/cm(J/M)ft·lb/in | ||
| Rockwell hardness | ASTM D785 | 75 | ||
| Bending modulus | ASTM D790/ISO 178 | 1.7(2.4) | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 410(5820) | kg/cm²(MPa)[Lb/in²] | |
| Flexural elasticity | ASTM D-790 | 1.7(2.4) | ||
| Rockwell hardness | ASTM D-785 | 75 | L | |
| bending strength | ASTM D-790 | 410(5820) | kg/cm | |
| Elongation rate | ASTM D-638 | 45 | % | |
| tensile strength | ASTM D-638 | 300(4260) | kg/cm | |
| IZOD impact strength | 1/4" | ASTM D-256 | 7.0(1.28) | kg.cm/cm(ft.lb/in) |
| 1/8" | ASTM D-256 | 8.5(1.56) | kg.cm/cm(ft.lb/in) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D-648 | 80(176) | ℃(°F) | |
| vicat softening point | ASTM D-1525 | 94(201) | ℃(°F) | |
| Combustion rate | File No E56070 UL&C-CL | 1/16"V0 | ||
| Combustibility (rate) | UL94 | 1/16"V0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 80(176) | ℃（℉） | |
| vicat softening point | ASTM D1525/ISO R306 | 94(201) | ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.