PC/PBT 6240-1001 SABIC INNOVATIVE CANADA

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedLow warpage

Typical Applications:

Automotive ApplicationsCastersPlastic bag

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Casters \| Plastic bag
Properties:	Glass fiber reinforced \| Low warpage

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
-30°C		ASTM D256	60	J/m
23°C		ASTM D256	86	J/m
-30°C		ISO 180/1A	7.0	kJ/m²
23°C		ISO 180/1A	7.0	kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	35.0	J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	56.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.800mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--8		ISO 178	101	Mpa
Yield, 50.0mm span		ASTM D790	96.0	Mpa
--1		ASTM D638	4350	Mpa
yield		ASTM D638	55.0	Mpa
yield	yield		ISO 527-2/5	56.0	Mpa
crack		ASTM D638	40.0	Mpa
crack	crack		ISO 527-2/5	29.0	Mpa
yield		ASTM D638	3.0	%
yield	yield		ISO 527-2/5	3.0	%
crack		ASTM D638	35	%
crack	crack		ISO 527-2/5	25	%
50.0mm span		ASTM D790	4400	Mpa
--7		ISO 178	4510	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
1.8MPa, unannealed, 6.40mm		ASTM D648	90.0	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	86.0	°C
Flow: -40 to 40 ° C		ASTME831	4.9E-05	cm/cm/°C
Flow: -40 to 40 ° C	Flow: -40 to 40 ° C		ISO 11359-2	4.8E-05	cm/cm/°C
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	6.4E-05	cm/cm/°C
Horizontal: -40 to 40 ° C	Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ISO 11359-2	6.3E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260°C/2.16kg	ASTM D1238	17	g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	15.0	cm3/10min
Shrinkage rate	MD	Internal Method	0.33	%
	Shrinkage rate	MD:3.20mm	Internal Method	0.30-0.40	%
	Shrinkage rate	Shrinkage rate	TD	Internal Method	0.38	%
Water absorption rate	Saturation,23°C	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.030	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.