Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.24 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10到15 g/10min |
| melt mass-flow rate | | ISO1133 | 15到30 g/10min |
| melt mass-flow rate | | ISO1133 | <0.40 % |
| melt mass-flow rate | | ISO1133 | >99 % |
| melt mass-flow rate | | ISO1133 | <250 ppm |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ISO14782 | >90.0 % |
| Haze ratio | | ISO14782 | <5.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 3500 MPa |
| Tensile stress | Yield | ISO527-2 | 60.0 MPa |
| Tensile stress | Break | ISO527-2 | 55.0 MPa |
| Tensile strain | Break | ISO527-2 | 6.0 % |
| Bending stress | | ISO178 | 90.0 MPa |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.08到1.12 g/cm³ |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 3.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO11357-2 | 52.0到60.0 °C |
| melting temperature | | ISO11357-3 | 145到175 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.