Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 10 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40 % |
| Water absorption rate | | ASTMD570 | 0.56 % |
| density | | ASTMD792 | 1.07 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 31 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTMD638 | 820 % |
| tensile strength | Yield | ASTMD638 | 14.0 MPa |
| Compression Modulus | | ASTMD695 | 2.40 MPa |
| | ASTMD1044 | 20.0 mg |
| Flexural modulus | | ASTMD790 | 23.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 无断裂 |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTMD412 | 3.40 MPa |
| tear strength | | ASTMD624 | 76.0 kN/m |
| compression set | | ASTMD395 | 49 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+12 ohms·cm |
| dielectric strength | | ASTMD149 | 20 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTMD1525 | 89.0 °C |
| melting temperature | | DSC | 180 °C |
| | ASTMD696 | 2E-04 cm/cm/°C |
| brittle temperature | | ASTMD746 | -65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.