Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.29 % |
| Water absorption rate | Saturation | ASTMD570 | 0.29 % |
| density | | ASTMD792,ISO1183 | 1.19到1.21 g/cm³ |
| melt mass-flow rate | | ASTMD1238,ISO1133 | 12 g/10min |
| Shrinkage rate | | ASTMD955 | 0.20到0.40 % |
| Water absorption rate | | ASTMD570,ISO62 | 0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ASTMD2863 | 24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 100 MPa |
| Bending stress | Break | ASTMD790 | 100 MPa |
| Tensile modulus | | ASTMD638,ISO527-2 | 4000 MPa |
| tensile strength | Yield | ASTMD638,ISO527-2 | 70.0 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 5.0 % |
| Flexural modulus | | ASTMD790,ISO178 | 4000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179,ASTMD256 | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179,ASTMD256 | 25 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256,ISO180 | 90 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 24 kV/mm |
| CTI | | IEC60112 | 150 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696 | 4E-05 cm/cm/°C |
| vicat | | ASTMD15255,ISO306/B505 | 134 °C |
| BallPressure Test | | VDE0470 | 通过 |
| | ASTMD648,ISO75-2/A | 120 °C |
| Continuous use temperature | | IEC60216 | 100 °C |
| vicat | | ASTMD15254,ISO306/A504 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.