PA6T R430NH

Form：Powder | Color：true qualities | Filler：glass fibre 30 %

Properties:

High temperature resistanFlame retardantHigh mobilityHigh rigiditywear resistantHigh impact resistance

Typical Applications:

Laptop caseFitness equipmentComputer caseEngine partsBottle capCasters

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Laptop case \| Fitness equipment \| Computer case \| Engine parts \| Bottle cap \| Casters
Properties:	High temperature resistan \| Flame retardant \| High mobility \| High rigidity \| wear resistant \| High impact resistance
Color:	true qualities
Form:	Pellets
Filler:	glass fibre 30%

Certificates

TDS

Technical Data Sheet

Other	Test Condition	Test Method	Test Result	Test Unit
防火等级		UL94	V-0
Hygroscopicity	平衡	ISO 62	0.3	%
Molding shrinkage rate		ISO 2577	0.8-1.0	%
Molding shrinkage rate	Molding shrinkage rate		ISO 2577	0.2-0.4	%
Fiberglass content			38	%
density		ISO 1183	1.48	g/cm³
Mechanical Properties	Test Condition	Test Method	Test Result	Test Unit
Tensile yield strength	2mm/min	ISO527-2	172	MPa
Flexural elasticity	2mm/min	ISO178	10082	MPa
Flexural strength	10mm/min	ISO 178	235	MPa
Gap cantilever beam impact test	23℃	ISO 180-1A	10	KJ/m²
Thermal Properties	Test Condition	Test Method	Test Result	Test Unit
Electrical strength		IEC60243-1	21	kV/mm
Volume resistivity		IEC60093	1015	Q·cm
Melt index	330℃/2.16KG		14.4	g/10min
Thermal distortion temperature	1.80MPa	ISO 75-2	265	℃
Thermal distortion temperature	Thermal distortion temperature	0.45MPa	ISO 75-2	285	℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.