Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	1000	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	900	N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	1.90	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	50	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	45	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm	UL 94	V-0
BurningBehavior		ISO 3795	passed
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	775	°C
		Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775	°C
		Hot filament ignition temperature	Hot filament ignition temperature	0.40mm	IEC 60695-2-13	850	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
		Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
		Burning wire flammability index	Burning wire flammability index	0.40mm	IEC 60695-2-12	960	°C
UL flame retardant rating	1.0mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	11000	Mpa
tensile strength	Break,23°C	ISO 527-2/5	150	Mpa
Tensile strain	Break,23°C	ISO 527-2/5	2.3	%
Bending modulus	23°C	ISO 178/A	10000	Mpa
bending strength	23°C	ISO 178/A	230	Mpa
Bending strain	23°C	ISO 178/A	2.5	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05	cm/cm/°C
Melting temperature		ISO 11357-3	222	°C
Vicat softening temperature		ISO 306/B120	205	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:280°C,2.00mm2	ISO 2577	0.60	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO 2577	0.30	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.10	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Volume resistivity	23°C	IEC 60093	3.4E+14	ohms·cm
Surface resistivity		IEC 60093	4.1E+13	ohms
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6.GFHR.14-110.GF25

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.