Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 262 °C |
| melting temperature | | ISO 11357-3 | 285 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | | ISO 4589-2 | 33 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.70 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2/1A/5 | 115 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.3 % |
| flexural modulus | 23°C | ISO 178 | 1280 MPa |
| bending strength | 23°C | ISO 178 | 178 MPa |
| tensile modulus | | ISO 527-2/1A/1 | 13000 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 26 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.