POM DURACON® KT-20

Properties:
wear resistant
High rigidity
enhance
currency
Usages:
Automotive sector
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.59 g/cm³
melt mass-flow rate		ISO1133	5.0 g/10min
Melt volume flow rate		ISO1133	3.70 cm3/10min
Shrinkage rate		ISO294-4	1.1 %
Shrinkage rate	Shrinkage rate		ISO294-4	1.1 %
Water absorption rate		ISO62	0.80 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO2039-2	90

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result
ColorNumber			CF2001

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2	8000 Mpa
Tensile stress		ISO527-2	91.0 Mpa
Tensile strain		ISO527-2	4.8 %
Flexural modulus		ISO178	7050 Mpa
Bending stress		ISO178	150 Mpa
		JISK7218	0.35
			JISK7218	0.36
Wear factor		JISK7218	<1.0 10^-8mm³/N·m
	Wear factor		JISK7218	200 10^-8mm³/N·m
		Wear factor		JISK7218	2500 10^-8mm³/N·m
		Wear factor	Wear factor		JISK7218	4000 10^-8mm³/N·m

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	3.5 kJ/m²

Electrical performance	Test Method	Test Result
Surface Resistivity	IEC60093	4E+15 ohms
Volume resistivity	IEC60093	4E+13 ohms·cm
dielectric strength	IEC60243-1	26 KV/mm

Test Method	Test Result
ISO75-2/A	145 °C
	内部方法	4E-05 cm/cm/°C
		内部方法	9E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

POM DURACON® KT-20