Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.30to0.50 % |
| Shrinkage rate | | | 0.30to0.50 % |
| Shrinkage rate | | | 0.14 % |
| melt mass-flow rate | | ISO1133 | 16 g/10min |
| Melt volume flow rate | | ISO1133 | 14.0 cm³/10min |
| density | | ISO1183 | 1.27 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2 | 4.8 % |
| Flexural modulus | | ISO178 | 2900 MPa |
| Bending stress | | ISO178 | 107 MPa |
| Tensile modulus | | ISO527-2 | 3500 MPa |
| Tensile stress | Break | ISO527-2 | 63.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 73 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 139 °C |
| | ISO75-2/A | 132 °C |
| | ISO11359-2 | 5E-05 cm/cm/°C |
| | ISO11359-2 | 5.9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare