ABS 3100M TAIDA TAIWAN

Form：Granules | Grade：Extrusion grade

Properties:

High impact resistanceHigh rigidityFatigue resistanceUltra high impact resistaHigh rigidityFatigue resistance

Typical Applications:

Footwear

Supplier(0)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Footwear
Properties:	High impact resistance \| High rigidity \| Fatigue resistance \| Ultra high impact resista \| High rigidity \| Fatigue resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	360	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	310	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 23℃	ASTM D790	58.6	Mpa
Impact strength of cantilever beam gap	23℃, 3.18 mm	ASTM D256	360	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃, 6.35 mm	ASTM D256	310	J/m
Rockwell hardness	R-Scale, 23℃	ASTM D785	100
tensile strength	Yield, 23℃, 3.18 mm	ASTM D638	38.6	Mpa
tensile strength	tensile strength	Break, 23℃, 3.18 mm	ASTM D638	31.7	Mpa
elongation	Break, 23℃, 3.18 mm	ASTM D638	40	%
Bending modulus	23℃	ASTM D790	2070	Mpa
tensile strength	Yield,23°C,3.18mm	ASTM D638	38.6	Mpa
tensile strength	tensile strength	Break,23°C,3.18mm	ASTM D638	31.7	Mpa
elongation	Break,23°C,3.18mm	ASTM D638	40	%
Bending modulus	23°C	ASTM D790	2070	Mpa
bending strength	Yield,23°C	ASTM D790	58.6	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Annealed, 12.7 mm	ASTM D648	85	°C
Vicat softening temperature		ASTM D1525	101	°C
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	85.0	°C
Vicat softening temperature		ASTM D15255	101	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.03	g/cm³
melt mass-flow rate	200℃/5.0 kg	ASTM D1238	0.6	g/10 min
melt mass-flow rate	melt mass-flow rate	220℃/10.0 kg	ASTM D1238	6	g/10 min
Shrinkage rate	MD	ASTM D955	< 0.40	%
Water absorption rate	Saturation	ASTM D570	< 0.30	%
density		ASTM D792	1.03	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	0.60	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	6.0	g/10min
Shrinkage rate	MD	ASTM D955	<0.40	%
Water absorption rate	Saturation	ASTM D570	<0.30	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App